• <pre id="q13ei"></pre>
    <acronym id="q13ei"><label id="q13ei"></label></acronym>
    <tr id="q13ei"><strong id="q13ei"><listing id="q13ei"></listing></strong></tr>
    1. <track id="q13ei"><ruby id="q13ei"></ruby></track>
      1. <acronym id="q13ei"><strong id="q13ei"><address id="q13ei"></address></strong></acronym>

        <td id="q13ei"><ruby id="q13ei"></ruby></td>
      2. 18839828187

        CN
        Refractory product series Auxiliary Material Series Feeder Head Product Series Functional Coatings Series Resin Product Series
        Cold box resin

        product details
        • Characteristics

          1. Low viscosity, good core sand mobility, lower sand shooting pressure and higher surface quality of sand core.

          2. Excellent demoulding performance, the core making efficiency has increased over 20%.

          3. The sand core has high initial strength, good deformation resistance, and less resin needed. 

          4. Higher resistance to moisture absorption, the storage time of the sand core is extended by 30%.

          5. High toughness when enduring pouring, lower scrap rate, and more accurate casting size;

          6. Low odor and less smoke, improve work conditions and make it more environmentally friendly.


        • Performance and specifications


          Component I(Phenolic resin)

          Component II(poly isocyanate)

          Appearance

          Light yellow to dark brown liquid

          brown liquid

          Density(20℃)g/cm3

          1.05~1.15

          1.05~1.20

          Viscosity(25℃)mPa.s

          ≤250

          ≤100


        • Use guide

          1.Sand mixing process

          The ratio of the two components can be adjusted within the range of 55/45 to 50/50. If there are more component I, the initial strength of the resin sand will be high; the total resin addition is generally 1.0-2.0% (accounting for the weight of the sand). In the batch sand mixer, the sand is mixed with component I for 1 minute, then component II is added and mixed for 2 minutes. After mixing, the sand could made into the core.

          2. Selection of technological parameters

          This series of products uses triethylamine hardening method to make cores. Triethylamine is mixed with the carrier gas and generally blown into the core box at a pressure of 0.2Mpa. The blowing time depends on the size and geometry of the sand core. It takes about 7 kg of carrier gas to transport 1 kg of triethylamine, to hardening 1 ton of core sand need about 0.45-0.8 kg of triethylamine.


        Product

        recommendation

        Email

        johnli.csm@gmail.com

        Technical advisor

        +86 18239875308

        Sales Manager

        +86 18239875308

        Whatsapp

        +86 18239875308

        WeChat

        +86 18239833671

        Copyright Sanmenxia Sunlight Casting Material Co.,Ltd.

        All Rights Reserved. Designed by Wanhu

        免费a级作爱片免费观看中国,欧美大片在线观看完整版,人妻丝袜av先锋影音先 免费a级作爱片免费观看中国,欧美大片在线观看完整版,人妻丝袜av先锋影音先,乌克兰美女的小嫩bbb,男人狂揉摸下面女人高潮,男人狂揉摸下面女人高潮

      3. <pre id="q13ei"></pre>
        <acronym id="q13ei"><label id="q13ei"></label></acronym>
        <tr id="q13ei"><strong id="q13ei"><listing id="q13ei"></listing></strong></tr>
        1. <track id="q13ei"><ruby id="q13ei"></ruby></track>
          1. <acronym id="q13ei"><strong id="q13ei"><address id="q13ei"></address></strong></acronym>

            <td id="q13ei"><ruby id="q13ei"></ruby></td>